Nail lacquer primary film forming resin

ABSTRACT

An improved nail lacquer containing a film forming resin, a plasticizer, and a solvent. The improvement resides in utilizing as the film forming resin a blend of: (i) a graft copolymer having a main backbone chain of acrylic ester units and methacrylic ester units, with the main backbone chain having grafted thereto pendant trialkoxysilyl groups and pendant ethylene glycol dimethacrylate groups; and (ii) a silsesquioxane resin containing RSiO 3/2  units and .tbd.SiOH units in which R is an alkyl group or an aryl group. In an alternate form of the invention, the film forming resin is not a blend, but an improved type of graft copolymer containing, in addition to pendant trialkoxysilyl groups, pendant vinylbenzyl chloride groups.

This is a divisional of copending application Ser. No. 08/026,706 filedon Mar. 5, 1993 now U.S. Pat. No. 5,302,379.

BACKGROUND OF THE INVENTION

This invention relates to a primary film forming resin for nail lacquersand nail enamel formulations and more particularly is directed to agrafted polymeric film forming resin for nail polish which will functionas a replacement for nitrocellulose.

Nail lacquers and enamels typically contain several ingredients amongwhich are a primary film former, secondary film formers, plasticizers,solvents, colorants, and fillers. In the past, nitrocellulose has beenthe primary film former employed in the majority of nail polishformulations but it suffers from the disadvantages that it is explosive;it tends to discolor as a function of time rendering it aestheticallydispleasing; and it is prone to undergo sharp changes in viscosity whichmake application difficult, Thus a need exists in the nail lacquer artsfor an improved primary film forming material.

Unlike copolymers having a linear arrangement of sequences such as-AAABBB- and -ABABAB-, graft copolymers are polymers in which themolecules are characterized by a main backbone chain to which sidechains containing different atomic constituents are attached at variouspoints along the main chain. For example a graft copolymer can berepresented by the structure ##STR1## The monomer units A and B arereferred to as the main chain or backbone, the sequence of C units isthe side chain or graft, and X is the unit in the backbone to which thegraft is attached.

Nail lacquers containing graft copolymers are not new. For example, inU.S. Pat. No. 5,153,268 issued Oct. 6, 1992, there is described a naillacquer formulation containing as the film forming resin a graftcopolymer having a main backbone chain of acrylic ester monomer unitsand methacrylic ester monomer units. Grafted to the main backbone chainare side chain units of carboxyl groups and side chain units oftrialkoxysilyl groups.

The present invention is an improvement in graft copolymers and naillacquers in accordance with the '268 patent. Accordingly, in the presentinvention ethylene glycol dimethacrylate side chain units are grafted tothe main backbone chain instead of carboxyl groups, and the resultinggraft copolymer is cold blended with a silsesquioxane resin. The blendedmaterial is useful as a film forming resin in nail lacquer applications.It possesses improved chip resistance, wearability, hardness, and gloss.The graft copolymer provides improved adhesion and the silsesquioxaneresin provides improved hardness for the nail lacquer system.

In an alternate embodiment of the invention, improved nail lacquer filmforming resins are obtained by grafting to the main backbone chain, inaddition to the trialkoxysilyl groups, side chain units of vinylbenzylchloride, instead of carboxyl groups as in the '268 patent. Such filmforming resins in accordance with this alternate embodiment have beenfound to possess significantly better adhesion characteristics than thecarboxyl group containing film forming resins of the '268 patent.

SUMMARY OF THE INVENTION

The invention is directed to a graft copolymer which has a main backbonechain of acrylic ester monomer units and methacrylic ester monomerunits. The main backbone chain has grafted thereto side chain units ofethylene glycol dimethacrylate groups and side chain units oftrialkoxysilyl groups. The copolymer is then cold blended with asilsesquioxane resin.

The invention is also directed to a nail lacquer which includes a filmforming resin, a plasticizer and a solvent. The improvement inaccordance with the present invention relates to the utilization as thefilm forming resin of the nail lacquer the graft copolymer blend notedabove.

Nail coat compositions containing the novel film forming resins andblends of the present invention have been found to provide improved wearresistance which is a highly desirable and sought after factor in thenail enamel market.

In an alternate embodiment, vinylbenzyl chloride groups are grafted tothe main backbone chain. These and other features, objects andadvantages of the herein described present invention will become moreapparent when considered in light of the following detailed description.

DETAILED DESCRIPTION OF THE INVENTION

Nail lacquer formulations exhibiting improved wear resistance areprovided herein by incorporating into nail care compositions as the filmforming ingredient a graft copolymer. The graft copolymer in accordancewith the present invention includes a main backbone chain of acrylicester monomer units and methacrylic ester monomer units. In addition themain backbone chain has grafted thereto side chain units of ethyleneglycol dimethacrylate groups and side chain units of trialkoxysilylgroups. The graft polymers of the present invention can be representedby the segment structure ##STR2## in which A represents an acrylatemonomer unit, B represents a methacrylate monomer unit, C represents anethylene glycol dimethacrylate group and D represents a trialkoxysilylgroup.

This random grafted copolymer contains in a typical segment of onehundred A and B units, thirty-three A units and sixty-seven B units.However in such a one hundred unit segment there is only one C unit andone D unit. The C and D units graft to only the A units. In other words,of one hundred "mer" units of the polymer there are sixty-seven B units,thirty-one A units, one A unit that has a C unit grafted thereto, andone A unit that has a D unit grafted thereto. The distribution of the"mer" units is random.

The acrylic ester monomer has the formula CH₂ ═CHCOOR in which R ispreferably an alkyl group having from one to sixteen carbon atoms. Themethacrylic ester monomer has the formula CH₂ ═C(CH₃)COOR' in which R'is an preferably an alkyl group having one to fourteen carbon atoms.Most preferred are main backbone chain copolymers in which the acrylicester monomer is butyl acrylate and the methacrylic ester monomer ismethyl methacrylate.

The ethylene glycol dimethyacrylate graft is formed by reacting the mainbackbone chain copolymer with ethylene glycol dimethacrylate in thepresence of a free radical initiator. The trialkoxysilyl graft is formedby reacting the main backbone chain copolymer with an acrylate or amethacrylate functional silane monomer in the presence of a free radicalinitiator. The grafts are formed by reacting the copolymer with ethyleneglycol dimethacrylate and the silane monomer in the presence of a freeradical initiator. The silane monomer is preferably3-methacryloxypropyltrimethoxysilane although there may also be employedmethacryloxypropenyltrimethoxysilane,3-methacryloxypropyltris(methoxyethoxy)silane, and3-acryloxypropyltrimethoxysilane.

While the most preferred monomers for the backbone chain copolymer arebutyl acrylate and methyl methacrylate, other combinations of acrylatesand methacrylates may be employed such as methyl, ethyl, propyl, pentyl,hexyl, octyl, nonyl, decyl, dodecyl, tetradecyl and hexadecyl acrylates;and ethyl, propyl, isopropyl, n-butyl, isobutyl, sec-butyl, t-butyl,n-hexyl, n-octyl, isooctyl, 2-ethylhexyl, n-decyl and tetradecylmethacrylates.

A particularly distinct advantage of the present invention is that thereis produced a material which contains less than about fen parts permillion of residual monomer. Thus a practically monomer free product isproduced by virtue of the fact that any residual monomer is grafted tothe polymer.

The improved film forming nail lacquer resins of the present inventionare made by mixing together an organic acrylate monomer, an organicmethacrylate monomer, a free radical initiator, and a solvent ester suchas ethyl acetate. The solution is heated for six to twelve hours atfifty to one hundred degrees Centigrade, accompanied with stirring at arate of one hundred to one thousand revolutions per minute. There isadded to the solution a trialkoxysilyl acrylate monomer and a freeradical initiator at room temperature. The concentration of thetrialkoxysilyl acrylate monomer relative to the acrylate/methacrylatecopolymer can be from 0.1 to 10.0 percent, but is preferably about threepercent. This is followed by addition to the solution of an ethyleneglycol dimethacrylate monomer together with a free radical initiator atroom temperature. The concentration of the ethylene glycoldimethacrylate monomer relative to the acrylate/methacrylate copolymercan also be from 0.1 to 10.0 percent, but is preferably about 1.5percent. A final product, in the form of a solution containing ten tofifty percent by weight, preferably thirty percent by weight of thegraft copolymer, is obtained by heating the solution for three to sixhours at a temperature of fifty to one hundred degrees Centigrade.

The graft copolymer solution is cold blended with a solution containinga silsesquioxane resin in an ester solvent such as ethyl acetate. Theconcentration of the silsesquioxane resin in the solution can be fromten to fifty percent, but is preferably about thirty percent. Thesolutions of the graft copolymer and the silsesquioxane resin areblended in a ratio of ten to fifty parts by weight of the graftcopolymer solution and fifty to ninety parts by weight of thesilsesquioxane resin solution.

The silicone resin used in accordance with the present invention is asilsesquioxane resin containing RSiO_(3/2) units and .tbd.SiOH units, inwhich R is an alkyl or aryl group such as methyl, ethyl, propyl, butyl,phenyl, or benzyl. Such resins and methods for their preparation areknown in the art, and are shown and described for example in U.S. Pat.No. 3,264,260 issued Aug. 2, 1966, and U.S. Pat. No. 5,075,103 issuedDec. 24, 1991.

One representative silicone resin and a particularly preferredsilsesquioxane resin is a material having the formula (PhSiO_(3/2))_(x)(PrSiO_(3/2))_(y) OH in which Ph is phenyl, Pr is propyl, and the ratioof x:y is 7:3. Another representative silsesquioxane resin is a materialhaving the formula (PhSiO_(2/2))_(a) (MePhSiO_(2/2))_(b)(PhSiO_(3/2))_(c) (MeSiO_(3/2))_(d) OH in which Ph is phenyl, Me ismethyl, and the ratio of the integers a:b:c:d is 10:5:40:45,respectively.

Suitable free radical initiators which may be employed include organicperoxides such as diacyl peroxides, peroxyesters, dialkyl peroxides, andperoxydicarbonates; and azo compounds. These initiators are known in theart and representative initiator compounds of the foregoing categoriesinclude dibenzoyl peroxide, t-butyl peroctoate, dicumyl peroxide,diisopropyl peroxydicarbonate, and 2,2'-azobis(isobutyronitrile),respectively.

In the case of the alternate embodiment of the invention, the sameprocedure is used, except that vinylbenzyl chloride is employed as themonomer for grafting instead of ethylene glycol dimethacrylate. Inaddition, the graft copolymer containing the vinylbenzyl chloridegrafted units is used without blending with the silsesquioxane resin.

The following examples are set forth in order to further illustrate theconcepts of the present invention.

EXAMPLE I

Into a three neck reaction flask containing 700 grams of ethyl acetatesolvent and three grams of t-butyl peroctoate free radical initiator,there was added and dissolved 204.63 grams of butyl acrylate and 81.18grams of methyl methacrylate. The solution was purged with argon forfifteen minutes. While stirring and maintaining an argon blanket, thesystem was heated to sixty degrees Centigrade for one hour, and thenheated to reflux at eighty degrees Centigrade for ten hours. Aftercooling to room temperature, there was added 4.86 grams of ethyleneglycol dimethacrylate and three grams of t-butylperoctoate initiator.The system was purged with argon for fifteen minutes, an argon blanketwas established, and the polymerization was allowed to proceed for fivehours at eighty degrees Centigrade. The flask was allowed to cool toroom temperature. To the solution was added 9.33 grams of3-methacryloxypropyltris(methoxyethoxy)silane and three grams of t-butylperoctoate initiator. After fifteen minutes of purging with argon, thegrafted copolymer solution in the flask was heated to eighty degreesCentigrade for five hours while maintaining the argon blanket. The flaskwas cooled to room temperature and contained 400 grams of the graftcopolymer.

EXAMPLE II

The 400 grams of graft copolymer produced in Example I was cold blendedwith 600 grams of a thirty percent solution of a silsesquioxane resin inethyl acetate. The silsesquioxane resin was a material having theformula (PhSiO_(3/2))_(x) (PrSiO_(3/2))_(y) OH in which Ph is phenyl, Pris propyl, and the ratio of x:y is 7:3. The blend was tested forhardness on glass in accordance with standard industry "Sward RockerHardness Test" which is used for measuring the hardness of organiccoatings. Basically, the Rocker device consists of two flat four inchchromium plated bronze rings spaced one inch apart. Amplitudes ofoscillation on a particular surface upon which it is placed areindicated by two tube style levels in the lower half of the Rocker. Inthe test, the swings are counted and multiplied by two to arrive at theRocker value.

The Sward Rocker Hardness values for the blend on glass after two hourswas eight, and after twenty-four hours was eleven. This is a significantimprovement over Rocker values of standard nitrocellulose based nailenamels which are typically anywhere in the range of 3-7 after twohours, and from 5-12 after twenty-four hours.

EXAMPLE III

The blend of Example II was tested for adhesion on glass in accordancewith the procedure of the standard industry "Cross-Cut Tape Test" setforth in the American Society for Testing and Materials designationunder the standard ASTM D3359-78. In this test, cross cuts are made inthe film to the substrate, pressure sensitive tape is applied over thecut and removed, and adhesion is assessed qualitatively on a scale offrom zero to five, with the value five being the best. Adhesion on glassfor the blend of Example II after twenty-four hours was five which iscomparable for adhesion values for nitrocellulose based nail enamels.

EXAMPLE IV

Examples I-III were repeated except that dibenzoyl peroxide was used asthe free radical initiator. The same hardness and adhesion values wereobtained as in the prior examples.

EXAMPLE V

Examples I-III were repeated except that butyl acetate was used as thesolvent. The hardness and adhesion values were comparable to the valuesobtained in the prior examples.

EXAMPLE VI

Examples I-III were repeated except that 100 grams of the graftcopolymer produced in Example I was cold blended with 900 grams of athirty percent solution of a silsesquioxane resin in ethyl acetate. Thesilsesquioxane resin was a material having the formula (PhSiO_(2/2))_(a)(MePhSiO_(2/2))_(b) (PhSiO_(3/2))_(c) (MeSiO_(3/2))OH in which Ph isphenyl, He is methyl, and the Patio of the integers a:b:c:d is10:5:40:45, respectively. The hardness value on glass after two hourswas sixteen, and the value after twenty-four hours was thirty-four. Theadhesion value on glass after twenty-four hours was five.

The following additional examples are set forth in order to illustratein more detail the alternate embodiment of the invention.

EXAMPLE VII

Into a three neck reaction flask containing 700 grams of ethyl acetatesolvent and six grams of t-butyl peroctoate free radical initiator,there was added and dissolved 126.69 grams of methyl methacrylate and66.183 grams of butyl acrylate. The solution was purged with argon forfifteen minutes. While stirring and maintaining an argon blanket, thesystem was heated to sixty degrees Centigrade for one hour, and thenheated to reflux at eighty degrees Centigrade for ten hours. Aftercooling to room temperature, there was added 9.825 grams of3-methacryloxypropyltris(methoxyethoxy)silane and three grams oft-butylperoctoate initiator. The system was purged with argon forfifteen minutes, an argon blanket was established, and thepolymerization was allowed to proceed for five hours at eighty degreesCentigrade. The flask was allowed to cool to room temperature. To thesolution was added 97.3 grams of vinylbenzyl chloride (H₂ C═CHC₆ H₄ CH₂Cl) and three grams of t-butyl peroctoate initiator. After fifteenminutes of purging with argon, the grafted copolymer solution in theflask was heated to eighty degrees Centigrade for five hours whilemaintaining the argon blanket. The ethyl acetate was stripped and freshethyl acetate was added to the flask. The flask was cooled to roomtemperature.

EXAMPLE VIII

The graft copolymer produced in Example VII was tested for hardness onglass in accordance with "Sward Rocker Hardness Test" in accordance withthe procedure explained in Example II. The Sward Rocker Hardness valuesfor this alternate form of graft copolymer on glass after two hours waseight, and after twenty-four hours was seventeen.

EXAMPLE IX

The graft copolymer of Example VII was tested for adhesion on glass inaccordance with the procedure of the "Cross-Cut Tape Test", the detailsof which are explained above in Example III. Adhesion on glass for thealternate form of graft copolymer after twenty-four hours was five whichis equivalent to one hundred percent adhesion. For purposes ofcomparison, the graft copolymers of the '268 patent were similarlytested for adhesion and exhibited an adhesion on glass after twenty-fourhours of twenty percent, which in accordance with the test, isequivalent to an adhesion value of zero. The zero value norm is used toindicate anything less than sixty-five percent.

The results of Example IX clearly indicate that graft copolymerscontaining along the main backbone chain grafted units of vinylbenzylchloride function remarkably better than the equivalent graft copolymerscontaining carboxyl units along the main backbone chain derived fromacrylic acid as in the '268 patent. This improvement is quiteunexpected, and is believed to be due to the fact that the activechlorine site in the grafted unit is capable of forming bonds with OHgroups available on the surface of the nail. Therefore, more durable andsubstantive films can be formed on the nails with this type of graftcopolymer. The improvement is also believed to be due to the fact thatthe active chlorine site in the grafted unit is capable of reacting withthe amino acids typically found in human finger and toe nails, resultingagain in more durable and substantive films. The amino acid compositionof a fingernail, for example, is 12 percent cystine, 8.5 percentarginine, 0.5 percent histidine, 2.5 percent tyrosine, 2.6 percentlysine, 1.1 percent tryptophan; with the remainder being represented byamino acids containing alkyl chains such as glycine, alanine, leucine,and valine.

Nail enamels in accordance with the present invention can be formulatedto include the grafted polymers and blends described above as theprimary film forming resin. In addition to the primary film formingresin the nail enamels require a plasticizer, a solvent and a colorant.

The plasticizer functions to control the flexibility and the elongationof the film. Plasticizers preferably should be nonvolatile, colorless,odorless and tasteless. Some examples of appropriate plasticizers whichmay be employed are dibutyl phthalate, tricresyl phosphate, dibutylphthalate, dibutyl glycolate, dioctyl phthalate, camphor, castor oil,benzyl benzoate, tributyl phosphate, butyl acetal ricenoleate, glycerylacetal ricenoleate, butyl stearate, tributoxy ethyl phosphate, triphenylphosphate, triethyl titrate, tributyl titrate, tributyl acetyl titrate,dibutyl tartarate, dimethoxy ethyl phthalate, and diamyl phthalate.

Solvents and diluents which may be used are acetone, ethyl acetate,butyl acetate, methyl glycol acetate, methyl ethyl ketone, methylisobutyl ketone, methyl acetate, toluene and xylene.

As a colorant there may be employed organic pigments such as TheCosmetics, Toiletries and Fragrance Association designated materials Dand C Red Nos. 5-7, 10-13 and 34, and D and C Yellow Nos. 5 and 6.Cosmetic grade inorganic pigments may also be employed such as yellowand red iron oxides, brown iron oxide, iron blue, iron black, carbonblack, purified titanium dioxide and bismuth oxychloride.

Nail lacquers and nail enamel formulations in accordance with thepresent invention contain six to thirty-five percent by weight of theprimary film forming resin, five to eight percent by weight of theplasticizer, sixty to eighty percent by weight of the solvent system andabout 0.05 to six percent by weight of colorant.

It will be apparent from the foregoing that many other variations andmodifications may be made in the compounds, compositions and methodsdescribed herein without departing substantially from the essentialfeatures and concepts of the present invention. Accordingly it should beclearly understood that the forms of the invention described herein areexemplary only and are not intended as limitations on the scope of thepresent invention as defined in the appended claims.

That which is claimed is:
 1. In a nail lacquer which includes a filmforming resin, a plasticizer, and a solvent, the improvement comprisingutilizing as the film forming resin a graft copolymer having a mainbackbone chain of acrylic ester units and methacrylic ester units, themain backbone chain having grafted thereto pendant trialkoxysilyl groupsand pendant vinylbenzyl chloride groups, the trialkoxysilyl grafts beinggrafted to only acrylic ester units and the vinylbenzyl chloride graftsbeing grafted to other of the remaining unsubstituted acrylic esterunits.
 2. A lacquer according to claim 1 in which the acrylic ester unitis formed from a precursor having the formula CH₂ ═CHCOOR in which R isan alkyl group having from one to sixteen carbon atoms, and themethacrylic ester unit is formed from a precursor having the formula CH₂═C(CH₃)COOR' in which R' is an alkyl group having one to fourteen carbonatoms.
 3. A lacquer according to claim 2 in which the acrylic esterunits are butyl acrylate and the methacrylic ester units are methylmethacrylate.
 4. A lacquer according to claim 1 in which thetrialkoxysilyl grafts are formed by reacting the main backbone chaincopolymer with an acrylate or methacrylate functional silane monomer inthe presence of a free radical initiator.
 5. A lacquer according toclaim 1 in which the solvent is an ester selected from the groupconsisting of methyl acetate, ethyl acetate, butyl acetate, and methylglycol acetate.
 6. A lacquer according to claim 5 which further includesa pigment.